Graphite emulsion
Graphite emulsionPerformanceBlack matrixOuter paintingInterior paintingSpray paintingBrush paintingLow resistanceG-102High resista…
Graphite emulsion Graphite emulsion for forging: MD-2 28 20 35 MD-3 30 25 MD-4 35 25 MD-6 40 25 40 MD-8 30 23 35 MD-10 35 26 MD-12 30 23 35 The indexes can be adjusted according to customers’ requirement.Performance Black matrix Outer painting Interior painting Spray painting Brush painting Low resistanceG-102 High resistanceGZ-303Y Mild flash overG-132 Solid content % 9.5±0.2% 35±3% 33±3% 34±4 41±2 39±2 Volatile content % 6±2 Ash % 86±3 PH value 10±0.5 9±1 Mucosity 25±5 300±100 350±50 25-40 23.0±2min 350±50 Resistivity Ω.cm ≤0.02 ≤0.02 <0.08 200-3000 2.5±0.5 Cohesiveness Okay Okay Okay Okay Porecreating Okay Wet fastness Okay Okay Granularity μm ≤1μm ≤30μm ≤30μm ≤15μm ≤10μm ≤10μm
Technical parameters of graphite emulsion for black and white kinescopeSpecification Solid content Volatile content PH value Mucosity mP.s Resistivity Cohesiveness Wet fastness Granularity μm Interior painting 35±3% 〈10% 80-100 〈0．08 Okay 〈15 Outer painting 38±3% 200-360 ≤0．05 Okay Okay 〈30 
The Ruisheng Brand graphite emulsion for forging is manufactured by our company with patented equipment and unique recipe. It is an ideal lubricant for high-temperature demoulding in hot processing of non-ferrous metals. The superior products are used in aviation and space flight as well as extrusion of warheads and cartridge cases. The products are warmly received by our customers.Types: MD-2、MD-3、MD-4、MD-6、MD-8、MD-10, MD-12Performance：With ideal high-temperature lubricity and cohesiveness, making demoulding easy. It is stable in chemical property, corrosive-less and toxic-less. It can improve the moulding quality and remarkably prolong the life of moulds.Purpose: It is an ideal lubricant for high-temperature demoulding in black and non-ferrous metal processing and is extensively used in forging and metal mould extrusion and processing. Main physical and chemical indexes:
Type
Property and its index
Examples of Application
Solid Content
(%)≮
Graphite Content
(%)≮
The Subsidency After
3 Hours Due to 20 Times of Dilution
(%)
Drop Forging,Roll Forging,Gear Rough and Finish Forge
Free of Dilution
Steel Casting
Free of Dilution
Purified Silicon Smelting
Light Alloy Extruding
Drop Forging for Heavy Pressor
Free of Dilution
Hot Extuding for Shell Case and Warhead
Hammer Forging